Monolayer Colloidal Aqueous Solution Ti2C MXenes

Details

Product Information:

Name: Monolayer colloidal solution Ti2CTx MXenes

Functional group: -OH F-O-Cl (customizable)

Size: Less than 500nm less than 200nm less than 100nm less than 50nm

Purity: 99%

Storage conditions: Low temperature dry seal must be stored in an inert atmosphere

Process: HF treatment or HCl+LiF treatment

MXenes material MXenes material

Name

Product name Craft

Processing

technology specifics

Details

Ti2C organ-like

Organoid material HF treatment

HF Treatment organoid material, obtained by etching with hydrofluoric acid.

Organ-like material obtained by etching with HF.

Single/little layer powder material

Single/Layer Powder Material freezing treatment

cryogenic treatment A colloidal solution of single/layer powder material, a powder obtained by freeze-drying. Powder obtained by freeze-drying of colloidal solution of single/small layer village material.

Nb2C organ-like

Organoid material HF treatment

HF Treatment organoid material, obtained by etching with hydrofluoric acid.

Organ-like material obtained by etching with HF.

Single/little layer powder material

Single/Layer Powder Material freezing treatment

Cryogenic treatment A colloidal solution of single/layer powder material, a powder obtained by freeze-drying. Powder obtained by freeze-drying of colloidal solution of single/small layer village material.

V2C organ-like

Organoid material HF treatment

HF Treatment organoid material, obtained by etching with hydrofluoric acid.

Organ-like material obtained by etching with HF.

Single/little layer powder material

Single/Layer Powder Material freezing treatment

cryogenic treatment A colloidal solution of single/layer powder material, a powder obtained by freeze-drying. Powder obtained by freeze-drying of colloidal solution of single/small layer village material.

Ti3C2 organ-like

Organoid material HF treatment

HF Treatment organoid material, obtained by etching with hydrofluoric acid.

Organ-like material obtained by etching with HF.

Clay material

Clay materials LiF treatment

LiF Treatment Clay materials can be dispersed into single layer materials by ultrasonic centrifugation, with a yield of about 25-35%. The ultrasonic power needs to be more than 160W, and the time is about 2h to 6h.

Clay material, which can be dispersed as a single layer material by ultrasonic centrifugation, yields about 25-35%. Ultrasound power needs more than 160W, and the time is about 2 h to 6 h.

Single/few layer colloidal solution

Single/Layer Colloidal Solution 5mg/ml

100ml single/little layer village compound colloidal solution, with the Tindahl phenomenon, can be directly utilized by the MXenes material.

The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.

The colloidal solution of single/few layer village material that has tindal

Single/Layer Colloidal Solution 10mg/ml

100ml single/little layer village compound colloidal solution, with the Tindahl phenomenon, can be directly utilized by MXenes material.

The colloidal solution of single/few layer village material that has Tindal phenomenon and can be used directly.

Single/few layer village material that has tindal

Single/Layer Powder Material

Freeze-drying

A colloidal solution of single/low-layer ingredients, a powder obtained by freeze-drying.

Powder obtained by freeze-drying of colloidal solution of single/small layer village material.

Self-supporting membrane material

Self-supporting membrane materials vacuum filtration

Vacuum suction filtration A colloidal solution of single/small layer village material, a flexible membrane obtained by vacuum suction filtration. Flexible membranes obtained from the colloidal solution of single/small-layer village materials by vacuum filtration.

Please refer to the attachment: MXene Manual for specific characterization